Wa Sun technology corp Co., Ltd. Tainan, Taiwan |
| Dear Wa Sun Tech： |
The LaQue Center has completed a 240-hour salt spray test on five (5) specimens. The specimens, supplied and identified by you, were received on June 17, 2002. The test was conducted in accordance with the ASTM B-117 Standard Practice for Operating Salt Spray (Fog) Apparatus. Table I summarizes conditions within the exposure cabinet during the test period. Panels were inspected for signs of corrosion initiation after 5-hours of testing, thereafter when the cabinet was opened for condensate analysis. If corrosion was noted on the bold surface the specimen was removed from test. Table II shows the removal time for each panel. |
| PO. Box 656 ․ 702 Causeway Drive ․ Wrightsville Beach, NC 28480-0656, USA |
| Phone：910.256.2271․ Fax：910.256.9816 |
| E-mail:uhon.chen@msa.hinet.net |
| Cabinet Temperature2 | 35.0°C ±0.1°C |
| Saturation Tower Temperature2 | 48.3°C ±0.3°C |
| Evaluation： | 1. Nifor - removed after 24 hours |
| 2. Ni - removed after 24 hours | |
| 3. Al Positive - removed after 240 hours | |
| 4. Fe Ni - iron corrosion at edges after 5 hours, no bold surface attack, specimen remained in test; removed after 240 hours | |
| 5. Cu Ni - removed after 240 hours | |
| 1. Atotech now known as Auto Technology Company Inc. | |
| 2. average for 240-hour test period | |
| UNTIL CORROSION | |
| PRODUCTS OBSERVED | |
| SPECIMEN | |
| SPECIMEN1 | REMOVED, hours |
| Al---Nifor | 24 |
| Al---Ni | 24 |
| Al---Positive | 240 |
| Al---Positive | 240 |
| Cu---Ni | 240 |
| 1.as identified by Mr. Wei-Ting Chen 2. iron corrosion observed at cut edges after 5 hours, no attack on bold surface; Specimen allowed to continue in test | |